Awards Nomination 20+ Million Readerbase
Google Scholar citation report
Citations : 1817

Dentistry received 1817 citations as per Google Scholar report

Flyer image
Dentistry peer review process verified at publons
Flyer image
Indexed In
  • Genamics JournalSeek
  • JournalTOCs
  • CiteFactor
  • Ulrich's Periodicals Directory
  • RefSeek
  • Hamdard University
  • EBSCO A-Z
  • Directory of Abstract Indexing for Journals
  • OCLC- WorldCat
  • Publons
  • Geneva Foundation for Medical Education and Research
  • Euro Pub
  • Google Scholar
View More
Useful Links
Share This Page
Journal Flyer
Flyer image
Open Access Journals
View More
Time domain analysis of de-bonding of composite-tooth interface using acoustic emission
Joint Event on 24th American Dental Research & Future Dentistry & 3rd Annual Meeting on Pedodontics and Geriatric Dentistry
May 25-26, 2018 New York, USA

Nak-Yeon Cho

Seoul National University, South Korea

Posters & Accepted Abstracts: Dentistry

Abstract:

The aim of this study was to evaluate the interfacial debonding behaviors of tooth-composite interface using an acoustic emission (AE) technique and relate it to the polymerization shrinkage kinetics of composites. An AE system was manufactured to detect the acoustic signals which were generated by the debonding at the tooth-composite interface during composite restoration. A class I cavity was prepared on the 14 extracted human premolars and divided into two groups. The prepared teeth in each group were restored with either a methacrylate based Z250 (3M ESPE) composite or a silorane based P90 (3M ESPE) composite. AE signals were measured as a function of time for 4000 s after the initiation of light curing. The polymerization shrinkage and peak shrinkage rate of two composites was measured. The mean of the total number of AE events for P90 was lower than that of Z250. AE in Z250 group was detected right after the beginning of light curing, while AE was first initiated 40 s after light exposure in P90. The polymerization shrinkage of P90 (1.34 %) was lower than that of Z250 (2.16 %). Peak polymerization shrinkage rate in P90 (0.247 %s-1) was also lower than that in Z250 (0.404 %s-1), and the time to reach peak shrinkage rate of P90 was longer (3.21 s) than that of Z250 (1.41 s). The lower the shrinkage (rate) and slower polymerization reaction of composites resulted in the lower AE events number. The AE is an effective technique to monitor the debonding kinetics at tooth-composite interface during the composite restoration in real time.